Firearms threat has always been a matter of personal concern, especially to soldiers in armed conflicts as well as police officers and civilians involved with public security. A multilayered armor system (MAS) is intended to personal protection against high kinetic energy ammunition, such as that used in rifles. MAS layers are normally composed of a front ceramic followed by a layer that must show both high impact resistance and low weight. Usually, synthetic fiber fabrics, such as aramid in Kevlar® and ultra-high molecular weight polyethylene (UHMWP) in Dyneema® are commonly used as the second layer. Currently, composites reinforced with natural fibers are also being considered as second MAS layer due to their good performance associated with the advantages of being cheaper and environmentally friendly. The fique is a relatively unknown natural fiber extracted from leaves of a plant native of South American Andes. In the present work, fique fibers and fique fabrics incorporated in polyester composite plates with volume fraction of 10, 20 and 30% were ballistic tested. The calculated projectile loss of energy indicated a relatively large energy dissipation by the composite. The tested specimens were statistically treated by the Weibull analysis and were examined by scanning electron microscopy.

Stainless steels are well known by their corrosion resistance. The austenitic types, in particular, are also applied as structural components in engineering systems operating at high temperatures such as nuclear reactors, petrochemical furnaces and turbines. For these applications operational temperatures may go up to 800ºC. Under constant load applications the main mechanism of failure, which would limit the material's life, is creep. In the present work creep parameters were evaluated in the high temperature interval of 600 to 800ºC for an AISI 316 austenitic stainless steel. Dislocation substructures were observed by transmission electron microscopy in creep ruptured specimens. Two distinct mechanisms of dynamic strain aging and dynamic recovery associated with different values for the power law exponent n and the Arrhenius activation energy Q for creep were verified below and above 700ºC, respectively.

Two distinct AISI type 316 stainless steels, of Brazilian and Swedish origins, were compared regarding their creep fracture mechanisms at 600, 700 and 800°C. The possible mechanisms associated with the creep fracture strength were identified by means of fracture maps proposed either by Ashby and collaborators or by Miller and Langdon. Experimental creep results were consistent with the general Ashby and collaborators map for face centered cubic alloys. By contrast, the two different 316 steel displayed significant differences in the model-based map of Miller and Langdon. In the present work, changes in the maps frontier are proposed as well as the introduction of a new field in the map related to grain boundary precipitation. These propositions allowed the Miller and Langdon map to be coherent with the experimental creep fracture results of both 316 stainless steels.

Natural fibers are attracting the interest of engineering sectors owing to specific advantages such as lightweight and lower cost as well as an inherent condition of being renewable, biodegradable, recyclable and environmentally correct with respect to CO2 emission. In addition, several natural fibers present mechanical and thermal properties appropriate for engineering applications. The fiber extracted from the stem of the banana plant is nowadays recognized by its mechanical properties. However, some thermal properties of the banana fibers have not yet been fully investigated. The present work investigated, by photoacoustic spectroscopy and photothermal techniques, the thermal diffusivity, specific heat capacity and thermal conductivity of the banana fiber. The results revealed that the banana fibers showed a promising thermal insulation capacity, comparable to those of conventional synthetic insulators.